TECHNICAL DATA  ::   
 

MAXFLEX® MAXFLEX® HT MAXFLEX® HF MAXFLEX® IsolOne
 Download MAXFLEX® Calculator
• MAXFLEX® Specification
PHYSICAL  PROPERTIES*
MAXFLEX
TEST  METHOD*
  Cell Structure
Closed Cell
-
  Density lbs/ft3 (g/cm3)
3-6 (0.048-0.096)**
 ASTM D 1667
 Thermal Conductivity      
BTU. in/ft 2 hr.°F (W/mK)
Mean
Temp.
- 4° F
( -20°C)
32° F
( 0°C)
75° F
( 24°C)
90° F
( 32°C)
 104° F
(40°C)
ASTM C177
JIS A1412
DIN 52613
K-Value
0.22
0.032
0.23
0.034
0.25
0.037
0.026
0.038
0.27
0.039
 Service Temperature***
 - 70°F  to  257°F
 - 57°C  to 125°C
 MAXFLAX  becomes hard at -57°C
but can be used even at -200°C
 Water Vapor Permeability (kg/Pa.s.m)
 0.10 perm-in (0.15 x 10-12)
 ASTM C 355
ASTM E96 ****
 Moisture Resistance ( µ Value)
 µ   not less than 5000
 DIN 52615
 Water Absorption (weight %)  
 not more than 3%
 ASTM D 1056
 Ozone Resistance
 No crack
 ASTM D 1171
 Heat Stability (% shrinkage)
 at 200°F and 220°F for 7 days
 4.5 and 5.5 respectively
 ASTM C 534
 Flammability & Smoke Density
Class VO
Self-extinguishing
Class 1
Class 0
Smoke density 80
UL - 94
ASTM D 635
BS476 Part 7 1987
BS476 Part 6 1987
ASTM-E84 (15mm thick)
  U.V.  Weather Resistance
 Excellent
 -
  Nitrosamine Contents
 Not detected
 U.S. FDA
  Flexibility
 Excellent
 -
Note :
* Figure show average values obtained by the world well-knowm testing institues.
** Average density of insulation thickness over 20 mm.
*** At temp . under -57 °C MAXFLEX® HF becomes hard, but it doesn't attect themal conductivity nor water vapor permeability.
**** Water vapor permeability test was done under test method ASTM E96 dehydrate test method at 37.8 °C
• MAXFLEX® HT Specification
PROPRIETA' FISICHE*
MAXFLEX-HT
METODO DI PROVA
ENTE CERTIFICANTE
MATERIALE EPDM GOMMA SINTETICA A BASE DI ETILENE, PROPILENE,DIENE MESCOLATI CON ADDITIVI    
STRUTTURA
CELLE COMPLETAMENTE CHIUSE
   
DENSITA' (g/cm3)

0.048 0.080**

 ASTM D 1667
PSB SINGAPORE

CONDUCIBILITA'
TERMICA, (W/m.K)

-20 'c
0 'c
24 'c
32 'c
4 0 'c

ASTM C177
JIS A 1412
DIN 52613

IBP GERMANA
0.031
0.033
0.036
0.037
0.038
TEMPERATURA DI ESERCIZIO FINO A 150 'C SERVIZIO CONTINUO    
FINO A 180 'C SERVIZIO INTERMITTENTE
PERMEABILITA AL VAPOR D'ACQUA (kg/Pa.s.m)
0.10 perm-in (0.15x10 -12)

 

ASTM C 355
ASTM E96
PSB SINGAPORE
RESISTENZA  ALLA UMIDITA

µ NON  INFERIORE A 10,000

DIN 52615
PSB SINGAPORE
ASSORBIMENTO D'ACQUA
(% IN PESO)
NON SUPERIORE AL 1.5%
ASTM D 1056
PSB SINGAPORE
RESISTENZA  ALL' OZONO
NON PRESENTA FESSURAZION
ASTM D 1171
PSB SINGAPORE
RESISTENZA  ALL'
INVECCHIAMENTO  A 160'C
NON PRESENTA FESSURAZION
ASTM C 534
PSB SINGAPORE
RESISTENZA  AI RAGGI  UV
NON PRESENTA FESSURAZION
ISO 4892-2
PSB SINGAPORE
STABILITA' AL CALORE
(% RITIRO IN PESO) A 95'C & 105'C PER 7 GIORNI
3.5 & 4.5
ASTM  C  534
PSB SINGAPORE
INFIAMMABILITA'  & DENSITA' FUMI
CLASSE VO
UL-94
PSB SINGAPORE
AUTOESTINGUENTE
ASTM D635
PSB SINGAPORE
CLASSE 1
BS 476 Part 7-1987
PSB SINGAPORE
CLASSE 0
BS 476 Part 6-1987
PSB SINGAPORE
CLASSE M1
AFNOR NF P92 501
CREPIMFRANCIA
CONTENUTO DI NITROSAMMINA
NO
BS EN 12868
PSB  SINGAPORE
RESISTENZA  A FUNGHI,MUFFE
PASSA
ASTM  G21
PSB  SINGAPORE
RIDUZIONE DEL RUMORE
36.3 db
DIN  52219
IBP
FLESSIBILITA'
ECCELLENTE
   
Note :
* VALORI MEDIATIOTTENUTI DA ENTI INTERNAZIONALI
** DENSITA & MEDIA PER SPESSORI SOPRA 20 mm.
• MAXFLEX® HF Specification
PHYSICAL PROPERTIES*
MAXFLEX® HF
TEST METHOD*
INSTITUTE
MATERIAL OF INSULATION
SYNTHETIC ELASTERMERIC WITHOUT CHLORIDE AND BROMIDE IONS
   
CELL STRUCTURE
COMPLETE CLOSED CELL
-
-
DENSITY lbs/ft3 (g/cm3)
3 ~ 5 ( 0.048 ~ 0.080 )
ASTM D 1667
PSB Corp., SINGAPORE
THERMAL CONDUCTIVITY BTU.in/ft2 hr. °F (W/m.K)
-4 °F
-20 °C
32 °F
0 °C
75 °F
24 °C
90 °F
32 °C
104 °F
40 °C
ASTM C177
JIS A 1412
DIN 52613
FIW MUNCHEN, GERMANY
0.22
0.031
0.23
0.033
0.25
0.036
0.26
0.037
0.27
0.038
SERVICE TEMPERATURE **
-57 °C to 150 °C
MAXFLEX® HF becomes hard at -57 °C but can be used even at -200 °C **
 
WATER VAPOR PERMEABILITY
(kg/Pa.s.m)
0.10 perm-in (0.15 x 10-12)
ASTM C 355
ASTM E96 ***
PSB Corp., SINGAPORE
MOISTURE RESISTANCE (µ Value)
µ not less than10,000
DIN 52615
PSB Corp., SINGAPORE
WATER ABSORPTION (weight %)
Not More Than 1.5%
ASTM D 1056
PSB Corp., SINGAPORE
OZONE RESISTANCE
Non crack
ASTM D 1171
PSB Corp., SINGAPORE
HEAT STABILITY (% Shrinkage) at 200 °F and 220 °F for 7 days
3.5 and 4.5 respectively
ASTM C 534
PSB Corp., SINGAPORE
ULTRA - VIOLET RESISTANCE
Non Crack
ISO 4892-2
PSB Corp., SINGAPORE
FIRE PERFORMANCE
Class VO
UL - 94
PSB Corp., SINGAPORE
Self-extinguishing
ASTM D635
PSB Corp., SINGAPORE
B2
DIN 4102
BODYCOTE, GERMANY
BEHAVIOR IN FIRE
Self-extinguting, does not spread flame, does not drip
-
-
NITROSAMINE CONTENTS
No Detect
BS EN 12868
PSB Corp., SINGAPORE
FUNGUS RESISTANCE
Passed
ASTM G21
PSB Corp., SINGAPORE
RIDUZIONE DEL RUMORE
36.3 db
DIN 52219
IBP, GERMANY
FLEXIBILITY
Excellent
-
-
STAINLESS STEEL AND COPPER CORROSION
Negligible
-
-
Note :
* Figure show average values obtained by the world well-knowm testing institues.
** At temp . under -57 °C MAXFLEX® HF becomes hard, but it doesn't attect themal conductivity nor water vapor permeability.
*** Water vapor permeability test was done under test method ASTM E96 dehydrate test method at 37.8 °C
• MAXFLEX® IsolOne Specification
PHYSICAL PROPERTIES*
MAXFLEX® IsolOne
TEST METHOD*
INSTITUTE
MATERIAL OF INSULATION
EDPM BLEND WITH ADDITIVE
   
CELL STRUCTURE
COMPLETE CLOSED CELL
-
 
DENSITY lbs/ft3 (g/cm3)
3 ~ 5 ( 0.048 ~ 0.080 )
ASTM D 1667
PSB Corp., SINGAPORE
THERMAL CONDUCTIVITY BTU.in/ft2 hr. °F (W/m.K)
-4 °F
-20 °C
32 °F
0 °C
75 °F
24 °C
90 °F
32 °C
104 °F
40 °C
ASTM C177
JIS A 1412
DIN 52613
FIW MUNCHEN, GERMANY
0.22
0.031
0.23
0.033
0.25
0.036
0.26
0.037
0.27
0.038
SERVICE TEMPERATURE **
up to 150 °C operating continuous
up to 180 °C operating intermitant
MAXFLEX® HF becomes hard at -57 °C but can be used even at -200 °C **
 
WATER VAPOR PERMEABILITY
(kg/Pa.s.m)
0.10 perm-in (0.15 x 10-12)
ASTM C 355
ASTM E96 ***
PSB Corp., SINGAPORE
MOISTURE RESISTANCE (µ Value)
µ not less than 10,000
DIN 52615
PSB Corp., SINGAPORE
WATER ABSORPTION (weight %)
Not More Than 1.5%
ASTM D 1056
PSB Corp., SINGAPORE
OZONE RESISTANCE
Non crack
ASTM D 1171
PSB Corp., SINGAPORE
AGING RESISTANCE AT 160 C. 150 hrs.
Non crack
ASTM 537
CERISIE, ITALY
ULTRA - VIOLET RESISTANCE
Non Crack
ISO 4892-2
CERISIE, ITALY
HEAT STABILITY (% Shrinkage) at 200 °F and 220 °F for 7 days
3.5 and 4.5 respectively
ASTM C 534
PSB Corp., SINGAPORE
FLAMMABILITY AND SMOKE DENSITY
Class VO
UL - 94
PSB Corp., SINGAPORE
Self-extinguishing
ASTM D635
PSB Corp., SINGAPORE
Class 1
BS 476 Part 7 1987
PSB Corp., SINGAPORE
Class 0
BS 476 Part 7 1987
PSB Corp., SINGAPORE
Class M1
FRANCE AFNOR NF P92 501
CREPIM, FRANCE
NITROSAMINE CONTENTS
No Detect
BS EN 12868
PSB Corp., SINGAPORE
FUNGUS RESISTANCE
Passed
ASTM G21
PSB Corp., SINGAPORE
NOISE REDUCTION
36.3 db
DIN 52219
IBP, GERMANY
FLEXIBILITY
Excellent
-
-
Note :
* Figure show average values obtained by the world well-knowm testing institues.
** At temp . under -57 °C MAXFLEX® HF becomes hard, but it doesn't attect themal conductivity nor water vapor permeability.
*** Water vapor permeability test was done under test method ASTM E96 dehydrate test method at 37.8 °C

 
 
VANDAPAC COMPANY LIMITED

93  Moo15  Watkingkaew Road, Bangpleeyai
Bangplee, Samutprakarn 10540, Thailand
Tel: 66-2312-4147-50, 2750-1560  Fax : 66-2312-4151

 

© 2004 Vandapac Company Limited. All Rights Reserved. Developed and hosted by w3solutionsweb.com